佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RC008H 含40%碳纤,导电,医疗级
LNP™ THERMOCOMP™ PA66 RC008H compound
聚酰胺66
40%碳纤维增强材料
SABIC Innovative Plastics
产品说明
LNP THERMOCOMP* RC008H is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
Also known as: LNP* THERMOCOMP* Compound RC-1008
Product reorder name: RC008H
UL黄卡 2：E121562-101282584
填料增强：含40%碳纤维增强
材料特点：导电
材料用途：医疗/护理领域的应用
塑料牌号：PA66 RC008H compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
|
|
-- |
1.33 |
g/cm³ |
ASTM D792 |
|
-- |
1.34 |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
0.20 到 0.40 |
% |
|
|
横向流动:24小时 |
0.40 到 0.60 |
% |
|
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.54 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.78 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量3 |
32000 |
MPa |
ASTM D638 |
|
抗张强度4(断裂) |
288 |
MPa |
ASTM D638 |
|
伸长率4(断裂) |
1.8 |
% |
ASTM D638 |
|
弯曲模量5(100 mm 跨距) |
26100 |
MPa |
ASTM D790 |
|
弯曲强度5(断裂,100 mm 跨距) |
429 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
110 |
J/m |
ASTM D256 |
|
23℃6 |
11 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
1200 |
J/m |
ASTM D4812 |
|
23℃6 |
71 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Total Energy |
15.8 |
J |
ASTM D3763 |
|
-- |
4.66 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,64.0 mm 跨距7 |
261 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
255 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距7 |
252 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
4.9E-6 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
0.000072 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
282 到 304 |
℃ |
|
|
模具温度 |
93.3 到 110 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|