佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RC008 含40%碳纤维增强 导电
LNP™ THERMOCOMP™ PA66 RC008 compound
聚酰胺66
40%碳纤维增强材料
SABIC Innovative Plastics
产品说明
LNP THERMOCOMP* RC008 is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive.
Also known as: LNP* THERMOCOMP* Compound RC-1008
Product reorder name: RC008
UL黄卡 2：E121562-101282584
填料增强：含40%碳纤维增强
材料特点：导电
塑料牌号：PA66 RC008 compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--3 |
30700 |
MPa |
ASTM D638 |
|
-- |
29500 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
断裂 |
267 |
MPa |
ASTM D638 |
|
断裂 |
294 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
断裂 |
1.9 |
% |
ASTM D638 |
|
断裂 |
1.7 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
-- |
23200 |
MPa |
ASTM D790 |
|
-- |
28400 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
440 |
MPa |
ASTM D790 |
|
-- |
458 |
MPa |
ISO 178 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.41 |
|
|
|
与自身-静态 |
0.30 |
|
|
|
磨损因数-Washer |
14.0 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
100 |
J/m |
ASTM D256 |
|
23℃4 |
11 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
1100 |
J/m |
ASTM D4812 |
|
23℃4 |
75 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击(23℃,Energy at Peak Load) |
9.60 |
J |
ASTM D3763 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
1.8 MPa,未退火,3.20 mm |
254 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距5 |
>240 |
℃ |
ISO 75-2/Af |
|
可燃性 |
额定值 |
|
测试方法 |
|
UL阻燃等级(1.50 mm,Testing by SABIC) |
HB |
|
UL 94 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
282 到 304 |
℃ |
|
|
模具温度 |
93.3 到 110 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|