佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RB006 含30%玻璃珠
LNP™ THERMOCOMP™ PA66 RB006 compound
聚酰胺66
30%玻璃珠
SABIC Innovative Plastics
产品说明
LNP* THERMOCOMP* RB006 is a compound based on Nylon 66 resin containing 30% Glass Bead.
Also known as: LNP* THERMOCOMP* Compound RB-1006
Product reorder name: RB006
填料增强：含30%玻璃珠
塑料牌号：PA66 RB006 compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
|
|
-- |
1.38 |
g/cm³ |
ASTM D792,ISO 1183 |
|
-- |
1.36 |
g/cm³ |
ASTM D792 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
1.0 到 3.0 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.72 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.72 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--2 |
6810 |
MPa |
ASTM D638 |
|
-- |
7290 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
断裂 |
66.9 |
MPa |
ASTM D638 |
|
断裂3 |
58.0 |
MPa |
ASTM D638 |
|
断裂 |
56.0 |
MPa |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
断裂 |
3.0 |
% |
ASTM D638 |
|
断裂3 |
6.5 |
% |
ASTM D638 |
|
断裂 |
7.6 |
% |
ISO 527-2/5 |
|
弯曲模量 |
|
|
|
|
-- |
4700 |
MPa |
ASTM D790 |
|
50.0 mm 跨距4 |
4060 |
MPa |
ASTM D790 |
|
--5 |
3850 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
ASTM D790 |
|
-- |
124 |
MPa |
|
|
断裂,50.0 mm 跨距4 |
87.0 |
MPa |
|
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
43 |
J/m |
ASTM D256 |
|
23℃6 |
3.6 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
390 |
J/m |
ASTM D4812 |
|
23℃6 |
25 |
kJ/m² |
ISO 180/1U |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,3.20 mm |
100 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火,64.0 mm 跨距7 |
101 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
92.7 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距7 |
95.0 |
℃ |
ISO 75-2/Af |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
282 到 304 |
℃ |
|
|
模具温度 |
93.3 到 110 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|