LNP STAT-LOY POM KX95702
LNP™ STAT-LOY™ Compound POM KX95702
Also known as:LNP™ Stat-loy™ Compound
PDX-K-95702 Product reorder name:KX95702
LNP STAT-LOY* KX95702 is a compound based on Acetal resin containing
Anti-Static. Added features of this material include: Antistat.
Property
TYPICAL PROPERTIES(1)
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,yield |
410 |
kgf/cm² |
ASTM D 638 |
|
Tensile Stress,break |
250 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,yield |
18.1 |
% |
ASTM D 638 |
|
Tensile Strain,break |
75.5 |
% |
ASTM D 638 |
|
Tensile Modulus,50mm/min |
15300 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
470 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
14100 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,yield |
41 |
MPa |
ISO 527 |
|
Tensile Stress,break |
31 |
MPa |
ISO 527 |
|
Tensile Strain,yield |
14.6 |
% |
ISO 527 |
|
Tensile Strain,break |
52.4 |
% |
ISO 527 |
|
Tensile Modulus,1mm/min |
1110 |
MPa |
ISO 527 |
|
Flexural Stress |
35 |
MPa |
ISO 178 |
|
Flexural Modulus |
1350 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
NB |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
16 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Energy @ peak,23℃ |
230 |
cm-kgf |
ASTM D 3763 |
|
Multiaxial Impact |
168 |
cm-kgf |
ISO 6603 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
NB |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
14 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
78 |
℃ |
ASTM D 648 |
|
CTE,-40℃ to 40℃,flow |
1.24E-04 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,xflow |
1.39E-04 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,flow |
1.24E-04 |
1/℃ |
ISO 11359-2 |
|
CTE,-40℃ to 40℃,xflow |
1.39E-04 |
1/℃ |
ISO 11359-2 |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
64 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.32 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
4.05 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs(5) |
1.7 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs(5) |
1.8 |
% |
ASTM D 955 |
|
Mold Shrinkage,flow,24 hrs(5) |
1.74 |
% |
ISO 294 |
|
Mold Shrinkage,xflow,24 hrs(5) |
1.83 |
% |
ISO 294 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Surface Resistivity |
1.E+09-1.E+11 |
Ohm |
ASTM D 257 |
|
Source GMD,last updated:2004/10/01 |
|||
|
Parameter Injection Molding |
Value |
Unit |
|
Drying Temperature |
80 |
℃ |
|
Drying Time |
4 |
hrs |
|
Melt Temperature |
195-205 |
℃ |
|
Front-Zone 3 Temperature |
200-210 |
℃ |
|
Middle-Zone 2 Temperature |
190-200 |
℃ |
|
Rear-Zone 1 Temperature |
175-190 |
℃ |
|
Mold Temperature |
70-95 |
℃ |
|
Back Pressure |
0.2-0.3 |
MPa |
|
Screw Speed |
30-60 |
rpm |