佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
POM KI001XXJ 硅酮润滑剂(2%),经润滑,耐磨损,医疗级
LNP™ LUBRICOMP™ POM KI001XXJ compound
聚甲醛（POM）共聚物
SABIC Innovative Plastics
产品说明
LNP* LUBRICOMP* KI001XXJ is a compound based on Acetal containing 2% Silicone. Added features of this grade include: Wear Resistant, Healthcare.
Also known as: LNP* LUBRICOMP* Compound KL-4410 HC
Product reorder name: KI001XXJ
含添加剂：硅酮润滑剂(2%)
性能特点：经润滑,耐磨损
材料用途：医疗/护理领域的应用
加工方法：注射成型
塑料牌号：POM KI001XXJ compound
定属记号：聚甲醛(POM)共聚物
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.40 |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
2.4 |
% |
|
|
横向流动:24小时 |
2.4 |
% |
|
|
吸水率(24 hr,50% RH) |
0.24 |
% |
ASTM D570 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量2 |
2750 |
MPa |
ASTM D638 |
|
抗张强度3 |
|
|
ASTM D638 |
|
屈服 |
55.0 |
MPa |
|
|
断裂 |
52.0 |
MPa |
|
|
伸长率3 |
|
|
ASTM D638 |
|
屈服 |
16 |
% |
|
|
断裂 |
46 |
% |
|
|
弯曲模量4(50.0 mm 跨距) |
2280 |
MPa |
ASTM D790 |
|
弯曲强度4(屈服,50.0 mm 跨距) |
74.7 |
MPa |
ASTM D790 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.44 |
|
|
|
与自身-静态 |
0.34 |
|
|
|
磨损因数-Washer |
22.0 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
82 |
J/m |
ASTM D256 |
|
无缺口悬臂梁冲击(23℃) |
1600 |
J/m |
ASTM D4812 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火,3.20 mm) |
106 |
℃ |
ASTM D648 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
螺筒后部温度 |
177 到 188 |
℃ |
|
|
螺筒中部温度 |
193 到 204 |
℃ |
|
|
螺筒前部温度 |
210 到 221 |
℃ |
|
|
加工(熔体)温度 |
199 到 216 |
℃ |
|
|
模具温度 |
82.2 到 110 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|