LNP STAT-LOY POM K3000
LNP™ STAT-LOY™ Compound POM K3000
Also known as:LNP™ Stat-loy™ Compound
K Product reorder name:K3000
LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing
Anti-Static. Added features of this material include: Antistat.
Property
TYPICAL PROPERTIES(1)
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,yield |
490 |
kgf/cm² |
ASTM D 638 |
|
Tensile Stress,break |
330 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,yield |
12 |
% |
ASTM D 638 |
|
Tensile Strain,break |
48 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
18600 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
560 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
17000 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,yield |
48 |
MPa |
ISO 527 |
|
Tensile Stress,break |
43 |
MPa |
ISO 527 |
|
Tensile Strain,yield |
12.1 |
% |
ISO 527 |
|
Tensile Strain,break |
28.6 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
1970 |
MPa |
ISO 527 |
|
Flexural Stress |
63 |
MPa |
ISO 178 |
|
Flexural Modulus |
1750 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
171 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
11 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Energy @ peak,23℃ |
241 |
cm-kgf |
ASTM D 3763 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
130 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
10 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,0.45 MPa,3.2 mm,unannealed |
150 |
℃ |
ASTM D 648 |
|
HDT,1.82 MPa,3.2mm,unannealed |
77 |
℃ |
ASTM D 648 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
132 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
76 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.35 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
1.8 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs(5) |
2-2.4 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs(5) |
1.9-2.4 |
% |
ASTM D 955 |
|
Mold Shrinkage,flow,24 hrs(5) |
2-2.4 |
% |
ISO 294 |
|
Mold Shrinkage,xflow,24 hrs(5) |
1.9-2.4 |
% |
ISO 294 |
|
Density |
1.35 |
g/cm³ |
ISO 1183 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Volume Resistivity |
1.E+10-1.E+11 |
Ohm-cm |
ASTM D 257 |
|
Surface Resistivity |
1.E+10-1.E+11 |
Ohm |
ASTM D 257 |
|
Source GMD,last updated:2008/09/24 |
|||
|
Parameter Injection Molding |
Value |
Unit |
|
Drying Temperature |
80 |
℃ |
|
Drying Time |
4 |
hrs |
|
Melt Temperature |
195-205 |
℃ |
|
Front-Zone 3 Temperature |
200-210 |
℃ |
|
Middle-Zone 2 Temperature |
190-200 |
℃ |
|
Rear-Zone 1 Temperature |
175-190 |
℃ |
|
Mold Temperature |
70-95 |
℃ |
|
Back Pressure |
0.2-0.3 |
MPa |
|
Screw Speed |
30-60 |
rpm |
|
|
||