佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RA2 耐磨损 含芳族聚酰胺纤维
LNP™ LUBRILOY™ PA66 RA2 compound
聚酰胺66
芳族聚酰胺纤维
SABIC Innovative Plastics
产品说明
LNP* LUBRILOY* RA2 is a compound based on Nylon 66 resin containing Aramid Fiber. Added feature of this material is: Wear Resistant.
Also known as: LNP* LUBRILOY* Compound RA
Product reorder name: RA2
填料增强：含芳族聚酰胺纤维
性能特点：耐磨损
塑料牌号：PA66 RA2 compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
ASTM D792 |
|
-- |
1.04 |
g/cm³ |
|
|
-- |
1.05 |
g/cm³ |
|
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
1.0 到 3.0 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
吸水率(24 hr,50% RH) |
0.20 |
% |
ASTM D570 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量2 |
6900 |
MPa |
ASTM D638 |
|
抗张强度3(断裂) |
68.0 |
MPa |
ASTM D638 |
|
伸长率3(断裂) |
4.0 |
% |
ASTM D638 |
|
弯曲模量4(50.0 mm 跨距) |
2620 |
MPa |
ASTM D790 |
|
弯曲强度 |
87.6 |
MPa |
ASTM D790 |
|
压缩强度 |
68.9 |
MPa |
Internal Method |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.66 |
|
|
|
与自身-静态 |
0.41 |
|
|
|
磨损因数-Washer |
5.00 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
69 |
J/m |
ASTM D256 |
|
无缺口悬臂梁冲击(23℃) |
590 |
J/m |
ASTM D4812 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火,3.20 mm) |
104 |
℃ |
ASTM D648 |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
4.0E-6 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
6.0E-6 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
277 到 288 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|