PA6 TG7S 含34%玻纤增强,抗冲击,热稳定
Ultramid® PA6 TG7S
聚酰胺6
玻璃纤维增强材料,34%
BASF Corporation
产品说明
Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to be made of an engineering plastic as opposed to metal. TG7S exhibits improved strength,stiffness and notched impact properties over Ultramid 8333G HI.
Applications
Include cushion seat pan/frame and other automotive seating applications, automotive fan, power tools and trimmer components.
UL 黄卡2：E36632-231205
填料增强：含34%玻璃纤维增强材料
含添加剂：冲击调节器，热稳定剂
材料特点：半结晶，尺寸稳定，低粘度，改良抗撞击，刚性佳，易加工，抗热老化，抗蠕变，流动性好，良好的强度，耐化学，耐磨蚀，热稳定，韧性良好
材料用途：动力/其它工具，汽车领域的应用，座椅
产品形式：颗粒料
外观颜色：自然色
加工方法：注射成型
塑料牌号：PA6 TG7S
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.37 |
g/cm³ |
ISO 1183 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸应力 |
|
|
ISO 527-2 |
|
断裂,-40℃ |
251 |
MPa |
|
|
断裂,23℃ |
170 |
MPa |
|
|
断裂,80℃ |
97.0 |
MPa |
|
|
断裂,121℃ |
77.0 |
MPa |
|
|
拉伸应变(断裂,23℃) |
3.3 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
8400 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
23 |
kJ/m² |
ISO 179 |
|
悬壁梁缺口冲击强度 |
|
|
ISO 180 |
|
-40℃ |
18 |
kJ/m² |
|
|
23℃ |
26 |
kJ/m² |
|
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火) |
203 |
℃ |
ISO 75-2/A |
|
溶融温度（DSC） |
220 |
℃ |
ISO 3146 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.080 |
% |
|
|
料筒后部温度 |
245 到 275 |
℃ |
|
|
料筒中部温度 |
260 到 285 |
℃ |
|
|
料筒前部温度 |
270 到 295 |
℃ |
|
|
射嘴温度 |
270 到 295 |
℃ |
|
|
加工（熔体）温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.