佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 R2000 经润滑,耐磨损
LNP LUBRILOY PA66 R2000 compound
聚酰胺66
SABIC Innovative Plastics
产品说明
LNP* LUBRILOY* R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Also known as: LNP* LUBRILOY* Compound R
Product reorder name: R2000
UL黄卡 2：E121562-101344544
含添加剂：润滑剂
性能特点：经润滑,耐磨损
塑料牌号：PA66 R2000 compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.03 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
1.8 到 2.2 |
% |
|
|
横向流动:24小时 |
2.1 到 3.1 |
% |
|
|
吸水率(24 hr,50% RH) |
0.25 |
% |
ASTM D570 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量3 |
2410 |
MPa |
ASTM D638 |
|
抗张强度 |
|
|
|
|
屈服 |
56.9 |
MPa |
ASTM D638 |
|
断裂 |
55.4 |
MPa |
ASTM D638 |
|
断裂 |
53.0 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
屈服 |
14 |
% |
ASTM D638 |
|
断裂 |
27 |
% |
ASTM D638 |
|
断裂 |
32 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
-- |
2320 |
MPa |
ASTM D790 |
|
-- |
2000 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
82.2 |
MPa |
ASTM D790 |
|
-- |
65.0 |
MPa |
ISO 178 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.36 |
|
|
|
与自身-静态 |
0.27 |
|
|
|
磨损因数-Washer |
50.0 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
62 |
J/m |
ASTM D256 |
|
23℃4 |
6.7 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
1700 |
J/m |
ASTM D4812 |
|
23℃4 |
140 |
kJ/m² |
ISO 180/1U |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
1.8 MPa,未退火,3.20 mm |
77.8 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距5 |
85.0 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM E831 |
|
流动:-40 到 40℃ |
0.000077 |
cm/cm/℃ |
|
|
横向:-40 到 40℃ |
0.00010 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
271 到 282 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|