PA6 HPN 9233G HS BK-102 含33%玻纤增强,高耐热,抗冲击,连接器
Ultramid® PA6 HPN 9233G HS BK-102
33%玻璃纤维增强材料
聚酰胺6
BASF Corporation
产品说明
Ultramid HPN 9233G HS BK-102 is a heat stabilized, pigmented black, 33% glass reinforced PA6 injection molding grade resin in the High Productivity Nylon Series developed for improved cycle times while maintaining excellent properties. It exhibits high strength, rigidity and heat resistance. Surface appearance has been improved, cycle times reduced and creep resistance retained. This heat stabilizer version extends the retention of mechanical properties at elevated temperatures while maintaining excellent chemical resistance to greases, oils and hydrocarbons.
Ultramid HPN 9233G HS BK-102 is generally recommended for applications such as window locks, valve bodies, chair shells, door and window hardware, connectors, switch components, relay parts, terminal blocks, power tool housings, gears, chainsaws, blowers, trimmer housings and automotive housings.
黄卡下载：E36632-231189
填料增强：含33%玻璃纤维增强
含添加剂：抗冲击剂，热稳定剂
材料特点：高刚性，高强度，抗蠕变，耐化学，高耐热，耐碳氢化合物，耐油，热稳定，生产阶段快
材料用途：齿轮，电气元件，动力/其它工具，阀门/阀门部件，开关，连接器，汽车领域的应用，外壳
产品形式：颗粒料
加工方法：注射成型
外观颜色：黑色
塑料牌号：PA6 HPN 9233G HS BK-102
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.39 |
g/cm3 |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.30 |
% |
|
|
吸水率 |
|
|
|
|
24 hr |
1.1 |
% |
ASTM D570 |
|
23℃,24 hr |
1.1 |
% |
ISO 62 |
|
饱和 |
6.4 |
% |
ASTM D570 |
|
饱和,23℃ |
6.4 |
% |
ISO 62 |
|
平衡,50% RH |
1.8 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.8 |
% |
ISO 62 |
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
120 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度(断裂,23℃) |
175 |
MPa |
ASTM D638,ISO 527-2 |
|
伸长率(断裂,23℃) |
3.0 |
% |
ASTM D638,ISO 527-2 |
|
弯曲模量 |
|
|
|
|
23℃ |
9380 |
MPa |
ASTM D790 |
|
23℃ |
8400 |
MPa |
ISO 178 |
|
弯曲强度(23℃) |
265 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
95 |
J/m |
ASTM D256 |
|
-40℃ |
7.0 |
kJ/m2 |
ISO 180 |
|
23℃ |
9.5 |
kJ/m2 |
ISO 180 |
|
Drop Impact Resistance(23℃) |
4.61 |
J |
内部方法 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火 |
174 |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
208 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
54.0 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
220 |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
3.8E-5 |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
UL 746 |
|
0.710 mm |
130 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
6.00 mm |
140 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.710 mm |
115 |
℃ |
|
|
1.50 mm |
115 |
℃ |
|
|
3.00 mm |
120 |
℃ |
|
|
6.00 mm |
120 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.710 mm |
140 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
6.00 mm |
140 |
℃ |
|
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
体积电阻率 |
|
|
|
|
1.50 mm |
> 1.0E+13 |
ohms·cm |
ASTM D257 |
|
-- |
> 1.0E+13 |
ohms·cm |
IEC 60093 |
|
介电强度3(1.50 mm) |
22 |
kV/mm |
ASTM D149 |
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
1.50 mm |
HB |
|
|
|
3.00 mm |
HB |
|
|
|
6.00 mm |
HB |
|
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
83.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 |
% |
|
|
加工（熔体）温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
|
备注： |
|||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.