PA6 BU50I 高抗冲击,耐低温撞击,汽车领域的应用
Ultramid® PA6 BU50I
聚酰胺6
BASF Corporation
产品说明
Ultramid Ultratough Nylon BU50I is an unreinforced PA6, impact modified injection molding product that maintains its impact strength and ductility to -40 deg F (-40 deg C). The extreme low temperature tolerance of Ultratough Nylon BU50I makes it ideal for applications in which the weldline impact strength at low temperatures is critical.
Ultramid BU50I is generally recommended for automotive components, small engines, power tool parts and casings, cold weather and high impact supports gear, such as snowboards, ski components, helmets and hockey masks.
黄卡下载：E36632-231173
含添加剂：冲击调节器
材料特点：超高韧性，改良抗撞击，高抗撞击，可焊接，耐低温，耐低温撞击，延展性
材料用途：Electric Motor Housings，安全帽，动力/其它工具，汽车领域的应用，体育用品
产品形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 BU50I
定属记号：尼龙6
物料数据
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
比重 |
1.06 |
-- |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
1.8 |
-- |
% |
|
|
吸水率 |
|
|
|
|
|
饱和 |
7.3 |
-- |
% |
ASTM D570 |
|
饱和,23℃ |
7.3 |
-- |
% |
ISO 62 |
|
平衡,50% RH |
2.1 |
-- |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
2.1 |
-- |
% |
ISO 62 |
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
1600 |
510 |
MPa |
ISO 527-2 |
|
抗张强度 |
|
|
|
|
|
屈服,23℃ |
50.0 |
-- |
MPa |
ASTM D638 |
|
屈服,23℃ |
45.0 |
27.0 |
MPa |
ISO 527-2 |
|
断裂,23℃ |
45.0 |
-- |
MPa |
ASTM D638 |
|
伸长率 |
|
|
|
|
|
屈服,23℃ |
5.0 |
-- |
% |
ASTM D638 |
|
屈服,23℃ |
4.0 |
42 |
% |
ISO 527-2 |
|
断裂,23℃ |
> 100 |
-- |
% |
ASTM D638 |
|
标称拉伸断裂应变(23℃) |
40 |
> 50 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
|
23℃ |
1690 |
-- |
MPa |
ASTM D790 |
|
23℃ |
1550 |
460 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
|
23℃ |
65.0 |
-- |
MPa |
ASTM D790 |
|
23℃ |
50.0 |
15.0 |
MPa |
ISO 178 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
95 |
-- |
kJ/m² |
ISO 179 |
|
简支梁无缺口冲击强度(23℃) |
无断裂 |
-- |
|
ISO 179 |
|
悬壁梁缺口冲击强度 |
|
|
|
ASTM D256 |
|
-40℃ |
无断裂 |
-- |
|
|
|
23℃ |
无断裂 |
-- |
|
|
|
落下冲击阻力(23℃) |
8.67 |
-- |
J/cm |
内部方法 |
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
载荷下热变形温度(1.8 MPa,未退火) |
50.0 |
-- |
℃ |
ASTM D648,ISO 75-2/A |
|
熔融峰值温度 |
220 |
-- |
℃ |
ASTM D3418,ISO 3146 |
|
RTI Elec |
|
|
|
UL 746 |
|
0.800 mm |
65.0 |
-- |
℃ |
|
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.800 mm |
65.0 |
-- |
℃ |
|
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.800 mm |
65.0 |
-- |
℃ |
|
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
可燃性 |
干燥 |
调节后的 |
|
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.800 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
2.0 到 4.0 |
hr |
||
|
建议的最大水分含量 |
0.15 |
% |
||
|
加工（熔体）温度 |
270 到 300 |
℃ |
||
|
模具温度 |
60.0 到 85.0 |
℃ |
||
|
注塑压力 |
3.50 到 12.5 |
MPa |
||
|
注射速度 |
快速 |
|
||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.