佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA6 8350 HS 高抗冲击,热稳定剂,低粘度 热稳定性 韧性良好 电缆护套
Ultramid® PA6 8350 HS
聚酰胺6
BASF Corporation
产品说明
Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility. It is also available in non-heat stabilized (Ultramid 8350) and/or pigmented versions.
Applications
Ultramid 8350 HS is generally recommended for applications such as automotive vacuum tubing, cable jacketing, and high pressure and hydraulic hoses.
黄卡下载：E36632-231157
含添加剂：冲击改性剂，热稳定剂
材料特点：低粘度，冲击改性，共聚物，良好的柔韧性，热稳定性，韧性良好
产品用途：电缆护套，管道，管件，汽车领域的应用，液压应用
颜色外观：白色，可用颜色，自然色
产品形式：颗粒料
加工方法：注射成型，挤出，型材挤出成型
塑料牌号：PA6 8350 HS
定属记号：尼龙6
物料数据
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
比重 |
1.07 |
-- |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率-流动(3.18 mm) |
1.4 |
-- |
% |
|
|
吸水率 |
|
|
|
|
|
24 hr |
1.1 |
-- |
% |
ASTM D570 |
|
23℃,24 hr |
1.1 |
-- |
% |
ISO 62 |
|
饱和 |
6.7 |
-- |
% |
ASTM D570 |
|
饱和,23℃ |
6.7 |
-- |
% |
ISO 62 |
|
平衡,50% RH |
1.9 |
-- |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.9 |
-- |
% |
ISO 62 |
|
硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
78 |
-- |
|
ASTM D785 |
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
ISO 527-2 |
|
-40℃ |
2150 |
-- |
MPa |
|
|
23℃ |
1800 |
675 |
MPa |
|
|
80℃ |
210 |
-- |
MPa |
|
|
121℃ |
150 |
-- |
MPa |
|
|
抗张强度 |
|
|
|
ASTM D638,ISO 527-2 |
|
屈服,-40℃ |
85.0 |
95.0 |
MPa |
|
|
屈服,23℃ |
53.0 |
32.0 |
MPa |
|
|
屈服,80℃ |
20.0 |
-- |
MPa |
|
|
屈服,121℃ |
14.0 |
-- |
MPa |
|
|
伸长率 |
|
|
|
|
|
屈服,-40℃ |
8.0 |
-- |
% |
ASTM D638 |
|
屈服,23℃ |
5.0 |
9.0 |
% |
ASTM D638,ISO 527-2 |
|
屈服,80℃ |
37 |
-- |
% |
ASTM D638 |
|
屈服,121℃ |
27 |
-- |
% |
ASTM D638 |
|
断裂,23℃ |
> 100 |
> 100 |
% |
ASTM D638 |
|
标称拉伸断裂应变(23℃) |
> 50 |
> 50 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
|
-40℃ |
2300 |
2760 |
MPa |
ASTM D790 |
|
23℃ |
1800 |
620 |
MPa |
ASTM D790 |
|
65℃ |
270 |
-- |
MPa |
ASTM D790 |
|
90℃ |
210 |
-- |
MPa |
ASTM D790 |
|
121℃ |
165 |
-- |
MPa |
ASTM D790 |
|
23℃ |
1750 |
-- |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
|
-40℃ |
120 |
120 |
MPa |
ASTM D790 |
|
23℃ |
65.0 |
30.0 |
MPa |
ASTM D790 |
|
65℃ |
20.0 |
-- |
MPa |
ASTM D790 |
|
90℃ |
10.0 |
-- |
MPa |
ASTM D790 |
|
121℃ |
10.0 |
-- |
MPa |
ASTM D790 |
|
23℃ |
50.0 |
-- |
MPa |
ISO 178 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
15 |
-- |
kJ/m² |
|
|
23℃ |
100 |
-- |
kJ/m² |
|
|
简支梁无缺口冲击强度(23℃) |
无断裂 |
-- |
|
ISO 179 |
|
悬壁梁缺口冲击强度 |
|
|
|
ASTM D256 |
|
-40℃ |
190 |
160 |
J/m |
|
|
23℃ |
无断裂 |
无断裂 |
|
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
载荷下热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
145 |
-- |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
56.0 |
-- |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
51.0 |
-- |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
220 |
-- |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数-流动 |
1.1E-4 |
-- |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
|
UL 746 |
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率 |
|
|
|
|
|
1.50 mm |
> 1.0E+13 |
-- |
ohms·cm |
ASTM D257 |
|
-- |
> 1.0E+13 |
-- |
ohms·cm |
IEC 60093 |
|
漏电起痕指数 |
600 |
-- |
V |
IEC 60112 |
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
挤出 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
2.0 到 4.0 |
hr |
||
|
建议的最大水分含量 |
0.10 |
% |
||
|
料筒1区温度 |
245 到 260 |
℃ |
||
|
料筒3区温度 |
240 到 255 |
℃ |
||
|
料筒5区温度 |
240 到 250 |
℃ |
||
|
法兰温度 |
225 到 240 |
℃ |
||
|
熔体温度 |
240 到 250 |
℃ |
||
|
头部温度 |
225 到 245 |
℃ |
||
|
口模温度 |
225 到 240 |
℃ |
||
|
挤出机螺杆长径比L / D |
20.0:1 to 24.0:1.0 |
|
||
|
挤出机螺杆压缩比 |
3.5:1.0 to 4.0:1.0 |
|
||
|
挤压说明 |
||||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.