PA6 8281 HS 经增塑,热稳定,热稳定 韧性良好
Ultramid® PA6 8281 HS
聚酰胺6
BASF Corporation
产品说明
Ultramid 8281 HS is an unreinforced, plasticized, heat stabilized nylon 6 rotomolding resin. Developed for applications requiring increased flexibility. It is also available in natural, black and can be painted. It exhibits excellent balance of engineering properties including strength, flexibility, and toughness combined with excellent abrasion resistance and self-lubricating properties associated with PA6. In addition, the heat stabilizer system extends its retention of properties at elevated temperatures. Chemical resistance is excellent to gasoline, diesel fuels, greases and oils. All data is from injection molded specimens with the exception of Drop Weight Impact.
Applications:Ultramid 8281 HS is generally recommended for applications such as fuel tanks, chemical storage tanks, hydraulic oil reservoirs, cyclones, heat resistance containers, and air ducts.
含添加剂：热稳定剂，增塑剂
材料特点：刚性好，高强度，经增塑，良好的柔韧性，耐化学，耐磨蚀，耐汽油，高耐热，耐油，耐油脂，热稳定，韧性良好，适于粉刷，自润滑
产品用途：工业容器，工用水箱，油箱
颜色外观：黑色，自然色
产品形式：颗粒料
加工方法：滚塑成型
塑料牌号：PA6 8281 HS
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
|
|
-- |
1.13 |
g/cm3 |
ASTM D792 |
|
-- |
1130 |
kg/m3 |
ISO 11832 |
|
吸水率 |
|
|
|
|
饱和 |
9.5 |
% |
ASTM D570,ISO 622 |
|
平衡,50% RH |
2.7 |
% |
ASTM D570 |
|
平衡 |
2.7 |
% |
ISO 622 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度 |
|
|
|
|
屈服,23℃,注塑 |
48 |
MPa |
ASTM D638 |
|
屈服 |
48 |
MPa |
ISO 527-22 |
|
伸长率(断裂,23℃,注塑) |
60 |
% |
ASTM D638 |
|
断裂伸长率 |
>50 |
% |
ISO 527-22 |
|
弯曲模量 |
|
|
ASTM D790 |
|
-40℃,注塑 |
3700 |
MPa |
|
|
23℃,注塑 |
1040 |
MPa |
|
|
65℃,注塑 |
320 |
MPa |
|
|
90℃,注塑 |
240 |
MPa |
|
|
121℃,注塑 |
225 |
MPa |
|
|
弯曲强度 |
|
|
ASTM D790 |
|
-40℃,注塑 |
175 |
MPa |
|
|
23℃,注塑 |
45 |
MPa |
|
|
65℃,注塑 |
20 |
MPa |
|
|
90℃,注塑 |
15 |
MPa |
|
|
121℃,注塑 |
15 |
MPa |
|
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃,注塑) |
80 |
J/m |
ASTM D256 |
|
Drop Impact Resistance(23℃) |
129 |
J |
Internal Method |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火,注塑) |
57 |
℃ |
ASTM D648 |
|
熔融峰值温度 |
220 |
℃ |
ASTM D3418,ISO 3146 |
|
RTI Elec(1.50 mm) |
65 |
℃ |
UL 746 |
|
RTI Imp(1.50 mm) |
65 |
℃ |
UL 746 |
|
RTI Str(1.50 mm) |
65 |
℃ |
UL 746 |
|
可燃性 |
额定值 |
测试方法 |
|
|
UL 阻燃等级(1.50 mm) |
HB |
UL 94 |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.2 |
% |
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.