PA6 8267G HS BK-106 含15%玻纤增强,含25%矿物,尺寸稳定 低翘曲 热稳定
Ultramid® PA6 8267G HS BK-106
聚酰胺6
玻璃纤维增强材料,15%; 矿物填料,25%
BASF Corporation
产品说明
Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The combination of mineral and glass fibers result in a high performance, low warp and cost effective engineering thermoplastic. It exhibits high strength, good UV resistance, rigidity and good heat distortion temperatures. It has a relatively high resistance to creep under load. The heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid 8267G HS BK-106 is generally recommended for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds and all external parts exposed to the environment.
填料增强：含15%玻璃纤维增强，含25%矿物填料
含添加剂：热稳定剂
材料特点：半结晶，尺寸稳定，低翘曲，低粘度，刚性好，高强度，抗弯曲，抗紫外线，可加工性好，表面光洁度佳，抗热老化，抗蠕变，流动性好，耐化学，耐磨蚀，热稳定
材料用途：把手，车轮，汽车领域的应用，室外应用
外观颜色：黑色
外观形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 8267G HS BK-106
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.48 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.40 |
% |
|
|
吸水率 |
|
|
|
|
24 hr |
0.90 |
% |
ASTM D570 |
|
23℃,24 hr |
0.90 |
% |
ISO 62 |
|
饱和 |
5.7 |
% |
ASTM D570 |
|
饱和,23℃ |
5.7 |
% |
ISO 62 |
|
平衡,50% RH |
1.6 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.6 |
% |
ISO 62 |
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
121 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
ISO 527-2 |
|
-40℃ |
10800 |
MPa |
|
|
23℃ |
9200 |
MPa |
|
|
80℃ |
3090 |
MPa |
|
|
121℃ |
2620 |
MPa |
|
|
抗张强度 |
|
|
|
|
断裂,-40℃ |
178 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,23℃ |
125 |
MPa |
ASTM D638 |
|
断裂,80℃ |
59.0 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,121℃ |
51.0 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,23℃ |
115 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
断裂,-40℃ |
3.0 |
% |
ASTM D638 |
|
断裂,23℃ |
2.0 |
% |
ASTM D638,ISO 527-2 |
|
断裂,80℃ |
13 |
% |
ASTM D638 |
|
断裂,121℃ |
11 |
% |
ASTM D638 |
|
弯曲模量 |
|
|
|
|
23℃ |
7580 |
MPa |
ASTM D790 |
|
23℃ |
7200 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
23℃ |
200 |
MPa |
ASTM D790 |
|
23℃ |
178 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
5.5 |
kJ/m² |
ISO 179 |
|
简支梁无缺口冲击强度(23℃) |
46 |
kJ/m² |
ISO 179 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
55 |
J/m |
ASTM D256 |
|
-40℃ |
4.0 |
kJ/m² |
ISO 180 |
|
23℃ |
6.0 |
kJ/m² |
ISO 180 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火 |
215 |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
202 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
200 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
220 |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
3.1E-5 |
cm/cm/℃ |
ASTM E831 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
83.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 |
% |
|
|
加工（熔体）温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.