PA6 8262G HS BK-125 加20%玻璃矿物增强,尺寸稳定 低翘曲 热稳定
Ultramid® PA6 8262G HS BK-125
聚酰胺6
20%玻璃矿物
BASF Corporation
产品说明
Ultramid 8262G HS BK-125 is a heat stabilized, pigmented black, 20% glass and mineral reinforced PA6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation.
Applications
Ultramid 8262G HS BK-125 is generally recommended for applications such as automotive housings, brackets, hubs, shrouds and roller bearings
填料增强：玻璃矿物,20%填料按重量
含添加剂：热稳定剂
材料特点：尺寸稳定性良好，低翘曲，热稳定
材料用途：外壳，汽车领域的应用，轴承
外观颜色：黑色
外观形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 8262G HS BK-125
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.29 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.80 |
% |
|
|
吸水率 |
|
|
|
|
24 hr |
1.3 |
% |
ASTM D570 |
|
23℃,24 hr |
1.3 |
% |
ISO 62 |
|
饱和 |
7.9 |
% |
ASTM D570 |
|
饱和,23℃ |
7.9 |
% |
ISO 62 |
|
平衡,50% RH |
2.2 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
2.2 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
5300 |
MPa |
ISO 527-2 |
|
抗张强度(断裂,23℃) |
100 |
MPa |
ASTM D638,ISO 527-2 |
|
伸长率(断裂,23℃) |
3.5 |
% |
ASTM D638,ISO 527-2 |
|
弯曲模量(23℃) |
4600 |
MPa |
ASTM D790,ISO 178 |
|
弯曲强度(23℃) |
160 |
MPa |
ASTM D790,ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
ISO 179 |
|
-30℃ |
3.0 |
kJ/m² |
|
|
23℃ |
3.3 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
35 |
J/m |
ASTM D256 |
|
-40℃ |
3.0 |
kJ/m² |
ISO 180 |
|
23℃ |
4.0 |
kJ/m² |
ISO 180 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火 |
211 |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
185 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
163 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
220 |
℃ |
ASTM D3418,ISO 3146 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
83.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 |
% |
|
|
加工（熔体）温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.45 到 10.3 |
MPa |
|
|
注射速度 |
快速 |
|
|