PA6 8232G HS FR BK-102 含25%玻纤增强,阻燃级,尺寸稳定 低粘度 连接器
Ultramid® PA6 8232G HS FR BK-102
聚酰胺6
玻璃纤维增强材料,25%
BASF Corporation
产品说明
Ultramid 8232G HS FR BK-102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.
Applications
Ultramid 8232G HS FR BK-102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.
黄卡下载：E36632-231124
含添加剂：热稳定剂
填料增强：含25%玻璃纤维增强材料
材料特点：尺寸稳定，低粘度，刚性高，高强度，较高的熔体稳定性，抗热老化，流动性好，耐磨蚀，阻燃级
材料用途：电器用具，开关，线轴，连接器，外壳
外观颜色：黑色
外观形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 8232G HS FR BK-102
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.62 |
g/cm3 |
ASTM D792 |
|
收缩率 - 流动(3.18 mm) |
0.30 |
% |
|
|
吸水率 |
|
|
ASTM D570 |
|
饱和 |
4.0 |
% |
|
|
平衡,50% RH |
1.1 |
% |
|
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
121 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度(断裂,23℃) |
145 |
MPa |
ASTM D638 |
|
伸长率(断裂,23℃) |
2.5 |
% |
ASTM D638 |
|
弯曲模量(23℃) |
9170 |
MPa |
ASTM D790 |
|
弯曲强度(23℃) |
210 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
80 |
J/m |
ASTM D256 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
载荷下热变形温度(1.8 MPa,未退火) |
205 |
℃ |
ASTM D648 |
|
熔融峰值温度 |
220 |
℃ |
ASTM D3418 |
|
RTI Elec |
|
|
UL 746 |
|
0.840 mm |
130 |
℃ |
|
|
1.50 mm |
130 |
℃ |
|
|
2.50 mm |
130 |
℃ |
|
|
3.00 mm |
130 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.840 mm |
115 |
℃ |
|
|
1.50 mm |
115 |
℃ |
|
|
2.50 mm |
115 |
℃ |
|
|
3.00 mm |
115 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.840 mm |
105 |
℃ |
|
|
1.50 mm |
115 |
℃ |
|
|
2.50 mm |
115 |
℃ |
|
|
3.00 mm |
120 |
℃ |
|
|
可燃性 |
额定值 |
|
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
0.840 mm |
V-0 |
|
|
|
1.50 mm |
V-0 |
|
|
|
2.50 mm |
V-0 |
|
|
|
5VA |
|
||
|
3.00 mm |
V-0 |
|
|
|
5VA |
|
||
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 |
% |
|
|
加工（熔体）温度 |
250 到 290 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.