/ Product details
/ classification
PA6 PX08322 compound 导热级,阻燃级
LNP™ KONDUIT™ PA6 PX08322 compound
聚酰胺6
矿物填料
SABIC Innovative Plastics
产品说明
LNP* KONDUIT* PX08322 is a compound based on PA6 resin containing mineral. Added features include: Thermally Conductive, Flame Retardant
Also known as: LNP* KONDUIT* Compound PX08322
Product reorder name: PX08322
填料增强：含矿物填料
材料特点：导热，阻燃
加工方法：注射成型
塑料牌号：PA6 PX08322 compound
定属记号：尼龙6
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.52 |
g/cm³ |
ASTM D792 |
|
熔流率(285℃/6.7 kg) |
15 |
g/10 min |
ASTM D1238 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
0.50 |
% |
|
|
横向流动:24小时 |
0.45 |
% |
|
|
吸水率 |
|
|
|
|
23℃,24 hr |
0.39 |
% |
Internal Method |
|
平衡,23℃,50% RH |
0.060 |
% |
ISO 62 |
|
UV Weathering-Start F1 from 1mm onword |
PASSES |
|
UL 746C |
|
Water Immersion-Start F1 from 1mm onword |
PASSES |
|
UL 746C |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量2 |
11800 |
MPa |
ASTM D638 |
|
抗张强度3(断裂) |
54.3 |
MPa |
ASTM D638 |
|
伸长率3(断裂) |
0.70 |
% |
ASTM D638 |
|
弯曲模量4(50.0 mm 跨距) |
11700 |
MPa |
ASTM D790 |
|
弯曲强度4(断裂,50.0 mm 跨距) |
82.0 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
17 |
J/m |
ASTM D256 |
|
无缺口悬臂梁冲击(23℃) |
88 |
J/m |
ASTM D4812 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火,6.40 mm) |
180 |
℃ |
ASTM D648 |
|
线形膨胀系数 |
|
|
ASTM E831 |
|
流动:-40 到 40℃ |
0.000022 |
cm/cm/℃ |
|
|
流动:40 到 120℃ |
0.000027 |
cm/cm/℃ |
|
|
横向:-40 到 40℃ |
0.000035 |
cm/cm/℃ |
|
|
横向:40 到 120℃ |
0.000058 |
cm/cm/℃ |
|
|
导热系数 |
|
|
|
|
--5 |
2.1 |
W/m/K |
ASTM E1461 |
|
--6 |
8.1 |
W/m/K |
ASTM E1461 |
|
--7 |
0.92 |
W/m/K |
ISO 22007-2 |
|
--8 |
5.1 |
W/m/K |
ISO 22007-2 |
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
表面电阻率 |
>1.0E+15 |
ohm |
ASTM D257 |
|
介电强度(1.00 mm,in Oil) |
14 |
kV/mm |
ASTM D149 |
|
介电常数 |
|
|
ASTM D150 |
|
50 Hz |
7.27 |
|
|
|
60 Hz |
7.27 |
|
|
|
1 MHz |
4.80 |
|
|
|
耗散因数 |
|
|
ASTM D150 |
|
50 Hz |
0.083 |
|
|
|
60 Hz |
0.083 |
|
|
|
1 MHz |
0.043 |
|
|
|
漏电起痕指数 |
575 |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
PLC 0 |
|
UL 746 |
|
热丝引燃(HWI) |
PLC 0 |
|
UL 746 |
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
UL 阻燃等级(1.20 mm) |
V-0 |
|
UL 94 |
|
灼热丝易燃指数(1.00 mm) |
960 |
℃ |
IEC 60695-2-12 |
|
热灯丝点火温度(1.00 mm) |
825 |
℃ |
IEC 60695-2-13 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 到 90.0 |
℃ |
|
|
干燥时间 |
3.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.010 |
% |
|
|
螺筒后部温度 |
230 到 270 |
℃ |
|
|
螺筒中部温度 |
240 到 280 |
℃ |
|
|
螺筒前部温度 |
250 到 280 |
℃ |
|
|
射嘴温度 |
250 到 280 |
℃ |
|
|
加工(熔体)温度 |
250 到 280 |
℃ |
|
|
模具温度 |
80.0 到 100 |
℃ |
|
|
背压 |
3.00 到 9.00 |
MPa |
|
|
螺杆转速 |
30 到 150 |
rpm |
|