PA6 PX00700 compound 含专有填料
LNP™ VERTON™ PA6 PX00700 compound
聚酰胺6
专有填料
SABIC Innovative Plastics (Americas)
产品说明
LNP VERTON* PX00700 is a compound based on Nylon 6 resin containing proprietary fillers. Added feature of this grade is: Structural.
Also known as:LNP™ VERTON™ Compound PDX-P-00700
Product reorder name:PX00700
增强填料：含专有填料
材料用途：构件
塑料牌号：PA6 PX00700
定属记号：尼龙6
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
188 |
MPa |
ISO 527 |
|
Tensile Strain,break |
2.7 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
9510 |
MPa |
ISO 527 |
|
Flexural Stress |
249 |
MPa |
ISO 178 |
|
Flexural Modulus |
8210 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched 80*10*4 +23℃ |
73 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
31 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
214 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
210 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.38 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
265-275 |
℃ |
|
|
Front-Zone 3 Temperature |
275-290 |
℃ |
|
|
Middle-Zone 2 Temperature |
265-275 |
℃ |
|
|
Rear-Zone 1 Temperature |
250-260 |
℃ |
|
|
Mold Temperature |
80-95 |
℃ |
|
|
Back Pressure |
0.3-0.7 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA6 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6 is among the most-used engineering materials, with excellent impact strength, moldability and paintability, fair heat resistance, and good wear and friction characteristics.