佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA6 PL002 compound 含10%PTFE润滑剂,经润滑,耐磨损
LNP™ LUBRICOMP™ PA6 PL002 compound
聚酰胺6
SABIC Innovative Plastics
产品说明
LNP* LUBRICOMP* PL002 is a compound based on Nylon 6 base resin containing 10% PTFE. Added feature of this grade is: Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound PL-4020
Product Reorder name: PL002
含添加剂：PTFE润滑剂(10%)
性能特点：经润滑,耐磨损
塑料牌号：PA6 PL002 compound
加工方法：注射成型
定属记号：尼龙6
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.19 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
1.0 到 3.0 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量2 |
3730 |
MPa |
ASTM D638 |
|
抗张强度3(断裂) |
52.7 |
MPa |
ASTM D638 |
|
伸长率3(断裂) |
25 |
% |
ASTM D638 |
|
弯曲模量4 |
2150 |
MPa |
ISO 178 |
|
弯曲强度 |
78 |
MPa |
ISO 178 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.6 |
|
|
|
与自身-静态 |
0.42 |
|
|
|
磨损因数 |
|
|
ASTM D3702 Modified |
|
Ring |
0.3 |
10^-10 in^5-min/ft-lb-hr |
|
|
Washer |
74 |
10^-10 in^5-min/ft-lb-hr |
|
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
48 |
J/m |
ASTM D256 |
|
23℃5 |
4.9 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
1200 |
J/m |
ASTM D4812 |
|
23℃5 |
68 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Total Energy |
9.6 |
J |
ASTM D3763 |
|
-- |
24.7 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,3.20 mm |
144 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火,64.0 mm 跨距6 |
133 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
54 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距6 |
51 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
0.000096 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
0.000095 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
249 到 260 |
℃ |
|
|
螺筒中部温度 |
266 到 277 |
℃ |
|
|
螺筒前部温度 |
277 到 288 |
℃ |
|
|
加工(熔体)温度 |
266 到 277 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.344 到 0.689 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|