PA6 PFD06 compound 含30%玻璃纤维增强,导电级
LNP™ STAT-KON™ PA6 PFD06 compound
聚酰胺6
玻璃纤维增强材料,30%
SABIC Innovative Plastics
产品说明
LNP* STAT-KON* PFD06 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Electrically Conductive.
Also known as: LNP* STAT-KON* Compound PF-30
Product reorder name: PFD06
填料增强：含30%玻璃纤维增强
性能特点：导电
塑料牌号：PA6 PFD06 compound
加工方法：注射成型
定属记号：尼龙6
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.43 |
g/cm³ |
ASTM D792 |
|
收缩率 |
|
|
|
|
流动:24小时 |
0.40 |
% |
ASTM D955 |
|
横向流动:24小时 |
1.2 |
% |
ASTM D955 |
|
横向流量:24小时 |
1.2 |
% |
ISO 294-4 |
|
流量:24小时 |
0.38 |
% |
ISO 294-4 |
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.50 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.91 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量2 |
11700 |
MPa |
ASTM D638 |
|
抗张强度(断裂) |
159 |
MPa |
ASTM D638 |
|
伸长率(断裂) |
2.3 |
% |
ASTM D638 |
|
弯曲模量 |
11000 |
MPa |
ASTM D790 |
|
弯曲强度 |
241 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
110 |
J/m |
ASTM D256 |
|
无缺口悬臂梁冲击(23℃) |
910 |
J/m |
ASTM D4812 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火,3.20 mm) |
206 |
℃ |
ASTM D648 |
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
表面电阻率 |
1.0 到 6.0 |
ohm |
ASTM D257 |
|
体积电阻率 |
1.0E+3 |
ohm·cm |
ASTM D257 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
249 到 260 |
℃ |
|
|
螺筒中部温度 |
266 到 277 |
℃ |
|
|
螺筒前部温度 |
277 到 288 |
℃ |
|
|
加工(熔体)温度 |
266 到 277 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.344 到 0.689 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|