PA6 PF008S compound 含40%玻璃纤维增强,热稳定
LNP™ THERMOCOMP™ PA6 PF008S compound
聚酰胺6
玻璃纤维增强材料,40%
SABIC Innovative Plastics
产品说明
LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized.
Also known as: LNP* THERMOCOMP* Compound PF-1008 HS
Product reorder name: PF008S
填料增强：含40%玻璃纤维增强
含添加剂：热稳定剂
材料特点：热稳定
塑料牌号：PA6 PF008S compound
加工方法：注射成型
定属记号：尼龙6
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.47 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 |
|
|
|
|
流动:24小时 |
0.20 到 0.40 |
% |
ASTM D955 |
|
横向流动:24小时 |
0.60 到 0.80 |
% |
ASTM D955 |
|
横向流量:24小时 |
0.60 到 0.80 |
% |
ISO 294-4 |
|
流量:24小时 |
0.20 到 0.40 |
% |
ISO 294-4 |
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.98 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.3 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--2 |
12700 |
MPa |
ASTM D638 |
|
-- |
13000 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
断裂 |
184 |
MPa |
ASTM D638 |
|
断裂 |
186 |
MPa |
ISO 527-2 |
|
伸长率(断裂) |
3.3 |
% |
ASTM D638,ISO 527-2 |
|
弯曲模量 |
|
|
|
|
-- |
9260 |
MPa |
ASTM D790 |
|
-- |
9530 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
279 |
MPa |
ASTM D790 |
|
-- |
278 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
130 |
J/m |
ASTM D256 |
|
23℃3 |
18 |
kJ/m² |
ISO 180/1A |
|
无缺口伊佐德冲击强度3(23℃) |
92 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Energy at Peak Load |
25.1 |
J |
ASTM D3763 |
|
-- |
21.6 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
1.8 MPa,未退火,3.20 mm |
196 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距4 |
208 |
℃ |
ISO 75-2/Af |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
249 到 260 |
℃ |
|
|
螺筒中部温度 |
266 到 277 |
℃ |
|
|
螺筒前部温度 |
277 到 288 |
℃ |
|
|
加工(熔体)温度 |
266 到 277 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.344 到 0.689 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|