PPS MT9203HS 热稳定,医疗级
FORTRON® MT® 9203HS SF3001 NATURAL
FORTRON MT9203HS | PPS | Medical Technology
Description
A very easy flowing, heat stabilized unfilled grade designed for melt blown processing suitable for medical/FDA applications.. This grade demonstrates excellent chemical resistance and thermal stability. Intended for extrusion applications that do not require high melt strength and for compounding with various fillers.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1350 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
4200 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
30 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
3900 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
130 |
MPa |
ISO 178 |
|
|
Unnotched impact str (Izod) @ 23℃ |
8 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
2 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
120 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
95 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.55 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.53 |
E-4/℃ |
ISO 11359-2 |
|
|
Eiec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Volume resistivity |
1E9 |
Ohm*m |
IEC 60093 |
|
|
Electric strength |
17 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
100 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
295 - 330 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Specific heat capacity of melt |
1830 |
J/(kg K) |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):130 - 140