PA66+PA6 84G33 BKB031 含33%玻纤增强,抗冲击
Zytel® 84G33 BKB031 | (PA66+PA6)-I-GF33 NYLON RESIN
Regional Availability
North America, South and Central America
Processing
Injection Moulding
Delivery form
Pellets
Product Text
Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.
The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
Zytel® 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was developed for applications requiring strength, stiffness and impact resistance along with good surface appearance.
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80℃
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
PROCESSING
Melt temperature optimum = 290℃
Melt temperature range = 280-300℃
Mould temperature optimum = 80℃
Mould temperature range = 50-100℃
PROPERTIES
|
Rheological properties |
dry / cond |
Unit |
Test Standard |
|
|
Rheo |
Moulding shrinkage,parallel |
0.1 / * |
% |
ISO 294-4,2577 |
|
Moulding shrinkage,normal |
0.6 / * |
% |
ISO 294-4,2577 |
|
|
Mechanical properties |
dry / cond |
Unit |
Test Standard |
|
|
Mech |
Tensile Modulus |
9000 / 6929 |
Mpa |
ISO 527-1/-2 |
|
Stress at break |
150 / 115 |
Mpa |
ISO 527-1/-2 |
|
|
Strain at break |
4 / 8.6 |
% |
ISO 527-1/-2 |
|
|
Flexural Modulus |
7680 / 5600 |
Mpa |
ISO 178 |
|
|
Charpy notched impact strength |
|
|
ISO 179/1eA |
|
|
23℃ |
21 / 20 |
kj/㎡ |
||
|
-40℃ |
11 / 10 |
kj/㎡ |
||
|
lzod notched impact strength |
|
|
ISO 180/1A |
|
|
23℃ |
21 / 23 |
kj/㎡ |
||
|
-40℃ |
15 / 53 |
kj/㎡ |
||
|
Hardness,Rockwell,M-scale |
81 / 53 |
- |
ISO 2039-2 |
|
|
Hardness,Rockwell,R-scale |
116 / 113 |
- |
ISO 2039-2 |
|
|
Thermal properties |
dry / cond |
Unit |
Test Standard |
|
|
Therm |
Melting temperature,10℃/min |
250 / * |
℃ |
ISO 11357-1/-3 |
|
Temp. of deflection under load,1.8 MPa |
222 / * |
℃ |
ISO 75-1/-2 |
|
|
Temp. of deflection under load,0.45 MPa |
247 / * |
℃ |
ISO 75-1/-2 |
|
|
Coeff. of linear therm. expansion,parallel |
15 / * |
E-6/K |
ISO 11359-1/-2 |
|
|
Coeff. of linear therm. expansion,normal |
120 / * |
E-6/K |
ISO 11359-1/-2 |
|
|
Flammability |
dry / cond |
Unit |
Test Standard |
|
|
Flam |
Burning Behav. at 1.5 mm nom. thickn. |
HB / * |
class |
IEC 60695-11-10 |
|
Thickness tested |
1.5 / * |
mm |
IEC 60695-11-10 |
|
|
Burning Behav. at thickness h |
HB / * |
class |
IEC 60695-11-10 |
|
|
Thickness tested |
0.8 / * |
mm |
IEC 60695-11-10 |
|
|
Electrical properties |
dry / cond |
Unit |
Test Standard |
|
|
Elec |
Comparative tracking index |
600 / - |
- |
IEC 60112 |
|
Other properties |
dry / cond |
Unit |
Test Standard |
|
|
Other |
Density |
1340 / - |
kg/m³ |
ISO 1183 |