POM TF-10XAP 低挥发,改良抗撞击性,良好的流动性
HOSTAFORM® TF-10 XAP® 14 BLACK
HOSTAFORM® TF-10 XAP® NATURAL
HOSTAFORM TF-10XAP® | POM | Impact Modified
Description
Hostaform® acetal copolymer TF-10 XAP® is low emission, improved flow, impact modified grade providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performance with improved impact in many applications.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1380 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
13 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.1 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.9 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
1750 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
49 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
13 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
1700 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
10 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
7 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
165 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
75 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 0.45 MPa |
139 |
℃ |
ISO 75-1/-2 |
Processing
Pre Drying
Drying is recommended.
Drying time (h)：3
Drying temperature (℃)：80 - 100