佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA6 SEG7 含35%玻纤增强,高强度,高流动,汽车领域的应用
Ultramid® PA6 SEG7
聚酰胺6
玻璃纤维增强材料,35%
BASF Corporation
产品说明
Ultramid SEG7 is a 35% glass reinforced, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness, and chemical resistance. It features superior flow properties, and is suited for parts having thinner walls and those requiring long lengths. It shows lower pressure, temperature, and cycle time requirements than conventional grades.
Applications
Applications include power tool, but can be used wherever strength and appearance are critical requirements, for example, automotive applications (door handles and mirrors).
黄卡下载：E36632-231203
填料增强：含35%玻璃纤维增强材料
材料特点：刚性佳，高强度，易加工，表面光洁度好，高流动，耐化学，韧性良好，生产阶段快
材料用途：薄壁部件，动力/其它工具，汽车领域的应用
机构评级：ULC Unspecified Rating
外观颜色：自然色
产品形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 SEG7
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.41 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.30 |
% |
|
|
吸水率 |
|
|
|
|
24 hr |
1.0 |
% |
ASTM D570 |
|
23℃,24 hr |
1.0 |
% |
ISO 62 |
|
饱和 |
6.3 |
% |
ASTM D570 |
|
饱和,23℃ |
6.3 |
% |
ISO 62 |
|
平衡,50% RH |
1.7 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.7 |
% |
ISO 62 |
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
120 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度(断裂,23℃) |
185 |
MPa |
ASTM D638,ISO 527-2 |
|
伸长率(断裂,23℃) |
3.5 |
% |
ASTM D638,ISO 527-2 |
|
弯曲模量(23℃) |
9670 |
MPa |
ASTM D790 |
|
弯曲强度(23℃) |
290 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
150 |
J/m |
ASTM D256 |
|
Drop Impact Resistance(23℃) |
3.80 |
J |
内部方法 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
熔融峰值温度 |
220 |
℃ |
ASTM D3418,ISO 3146 |
|
RTI Elec |
|
|
UL 746 |
|
0.710 mm |
130 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.710 mm |
115 |
℃ |
|
|
1.50 mm |
115 |
℃ |
|
|
3.00 mm |
120 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.710 mm |
120 |
℃ |
|
|
1.50 mm |
120 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
可燃性 |
额定值 |
|
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
1.50 mm |
HB |
|
|
|
3.00 mm |
HB |
|
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
83.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 |
% |
|
|
加工（熔体）温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.