PA6 HPN 9362 含40%矿物,抗冲击,热稳定,汽车领域的应用
Ultramid® PA6 HPN 9362
聚酰胺6
矿物填料,40%
BASF Corporation
产品说明
Ultramid HPN 9362 is a 40% mineral reinforced, impact modified PA6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing cycle time. It possesses excellent balance of strength, stiffness and toughness combined with a high level of drop weight impact, excellent processability and chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid HPN 9362 is generally recommended for applications such as wheel cover and hubs, mirror housings, appliance components, power tool housings, small engine pulleys, and trimmer spools.
黄卡下载：E36632-231190
含添加剂：冲击改性剂，热稳定剂
填料增强：含40%矿物填料
材料特点：尺寸稳定，低粘度，高刚高强度，表面光洁度佳，易加工，流动性佳，耐碳氢化合物，耐化学，耐油脂，耐磨蚀，热稳定，生产阶段快
材料用途：草坪和园林设备，家电部件，动力/其它工具，汽车领域的应用，外壳
机构评级：ULC Unspecified Rating
产品形式：颗粒料
加工方法：注射成型
外观颜色：可用颜色，自然色
塑料牌号：PA6 HPN 9362
定属记号：尼龙6
物料数据
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
比重 |
1.41 |
-- |
g/cm3 |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
1.0 |
-- |
% |
|
|
吸水率 |
|
|
|
|
|
饱和 |
4.9 |
-- |
% |
ASTM D570 |
|
饱和,23℃ |
4.9 |
-- |
% |
ISO 62 |
|
平衡,50% RH |
1.4 |
-- |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.4 |
-- |
% |
ISO 62 |
|
硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
119 |
-- |
|
ASTM D785 |
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
4330 |
2900 |
MPa |
ISO 527-2 |
|
抗张强度 |
|
|
|
|
|
屈服,23℃ |
64.0 |
45.0 |
MPa |
ASTM D638 |
|
屈服,23℃ |
65.0 |
45.0 |
MPa |
ISO 527-2 |
|
断裂,23℃ |
62.0 |
45.0 |
MPa |
ASTM D638 |
|
伸长率 |
|
|
|
|
|
屈服,23℃ |
3.0 |
27 |
% |
ASTM D638,ISO 527-2 |
|
断裂,23℃ |
15 |
30 |
% |
ASTM D638 |
|
弯曲模量 |
|
|
|
ASTM D790 |
|
-40℃ |
5230 |
-- |
MPa |
|
|
23℃ |
4000 |
1560 |
MPa |
|
|
65℃ |
1250 |
970 |
MPa |
|
|
90℃ |
770 |
850 |
MPa |
|
|
121℃ |
750 |
740 |
MPa |
|
|
弯曲强度 |
|
|
|
ASTM D790 |
|
-40℃ |
180 |
155 |
MPa |
|
|
23℃ |
109 |
50.0 |
MPa |
|
|
65℃ |
45.0 |
35.0 |
MPa |
|
|
90℃ |
30.0 |
30.0 |
MPa |
|
|
121℃ |
30.0 |
25.0 |
MPa |
|
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
3.0 |
-- |
kJ/m2 |
|
|
23℃ |
6.0 |
-- |
kJ/m2 |
|
|
悬壁梁缺口冲击强度(23℃) |
86 |
-- |
J/m |
ASTM D256 |
|
Drop Impact Resistance(23℃) |
74.6 |
-- |
J |
内部方法 |
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
载荷下热变形温度(1.8 MPa,未退火) |
80.0 |
-- |
℃ |
ASTM D648 |
|
熔融峰值温度 |
220 |
-- |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
2.3E-5 |
-- |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
65.0 |
-- |
℃ |
|
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
65.0 |
-- |
℃ |
|
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.750 mm |
65.0 |
-- |
℃ |
|
|
1.50 mm |
65.0 |
-- |
℃ |
|
|
3.00 mm |
65.0 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率 |
|
|
|
|
|
1.50 mm |
> 1.0E+13 |
-- |
ohms·cm |
ASTM D257 |
|
-- |
> 1.0E+13 |
-- |
ohms·cm |
IEC 60093 |
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
83.0 |
℃ |
||
|
干燥时间 |
2.0 到 4.0 |
hr |
||
|
建议的最大水分含量 |
0.15 |
% |
||
|
加工（熔体）温度 |
270 到 295 |
℃ |
||
|
模具温度 |
80.0 到 95.0 |
℃ |
||
|
注塑压力 |
3.50 到 12.5 |
MPa |
||
|
注射速度 |
快速 |
|
||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.